Self-leveling Cement Screed
YY-100 (General Purpose); YY-110 (Wear Resistant); YY-082 (Super Weather ability)
Scope of Application
YY-100 is suitable for indoor use, level the concrete floor before tiling, carpet floor, PVC floor and wood floor for the housing, offices, commercial places.
YY-110 is suitable for indoor use, level the concrete floor before finished painting for parking lot, garage and industrial factory use.
YY-082 is suitable for indoor and outdoor use, level the concrete floor or repair the tiling floor especially for the corridors, square,pavement,garage and high load industrial factory use.
Service: One stop solution package service.
Payment: 50% of total amount for deposit, balance before load.
Place of origin: Guangdong, China(mainland).
Supply ability: 100,000kgs per day.
Usage: 1.6kg/mm/㎡.
Material: Polymer cement based.
| CAS# | Chemical Name | % |
|---|---|---|
|
65997-15-1 |
Portlant Cement 42.5R |
25-35% |
|
14808-60-7 |
Silicone Sand |
35-45% |
|
1318-16-7 |
Bauxite Cement |
10-20% |
|
Mixture |
Polymer additive |
2-2.9% |
Delivery: 15-20 days.
Packing: 20kg/bag or 25kg/bag.
MOQ: 1000bags.
Technical Data
|
YY-100 (General Purpose) |
|
|
Status |
Single component |
|
Water Ratio |
22% |
|
Density of dry mortar |
≈1.3kg/L |
|
Density of freshly mixed glue |
≈2.0kg/L |
|
Working time |
20-30min |
|
Time of upper finishing |
24-48hours |
|
Fluidity ratio (mm) Initial value |
≥130 |
|
20min |
≥130 |
|
Tensile adhesion strength Mpa |
≥1.0 |
|
Wear resistant test g |
≤0.5 |
|
Dimensional change rate % |
-0.15~+0.15 |
|
Impact resistant test |
No crack or peeling from base |
|
Rub fastness |
Passed (BS 8204:AR1) |
|
Construction |
Grouting |
|
Compressive strength force 24h |
4.3Mpa |
|
Compressive strength force 7d |
17.5Mpa (En196) |
|
Compressive strength force 28d |
21Mpa |
|
Bending strength force 24h |
1.1Mpa |
|
Bending strength force 7d |
4.2Mpa(En196) |
|
Bending strength force 28d |
5.3Mpa |
|
Falling ball rigidity 24h |
25Mpa |
|
Falling ball rigidity 7d |
60Mpa(Brine 11) |
|
Shelf life |
12 months |
|
Condition on site |
5-40℃ |
|
YY-110 (Wear Resistant) |
|
|
Status |
Single component |
|
Water Ratio |
22% |
|
Density of dry mortar |
≈1.3kg/L |
|
Density of freshly mixed glue |
≈2.0kg/L |
|
Working time |
20-30min |
|
Time of upper finishing |
24-48hours |
|
Fluidity ratio (mm) Initial value |
≥130 |
|
20min |
≥130 |
|
Tensile adhesion strength Mpa |
≥1.0 |
|
Wear resistant test g |
≤0.5 |
|
Dimensional change rate % |
-0.15~+0.15 |
|
Impact resistant test |
No crack or peeling from base |
|
Rub fastness |
Passed (BS 8204:AR1) |
|
Construction |
Grouting |
|
Compressive strength force 24h |
15Mpa |
|
Compressive strength force 7d |
30Mpa (En196) |
|
Compressive strength force 28d |
40Mpa |
|
Bending strength force 24h |
5Mpa |
|
Bending strength force 7d |
8Mpa(En196) |
|
Bending strength force 28d |
12Mpa |
|
Falling ball rigidity 24h |
50Mpa |
|
Falling ball rigidity 7d |
55Mpa(Brine 11) |
|
Falling ball rigidity 28d |
80Mpa |
|
Shelf life |
12 months |
|
Condition on site |
5-40℃ |
|
YY-082(Super Weather ability) |
|
|
Status |
Double component |
|
Powder : latex |
100: 24 |
|
Density of dry mortar |
≈1.3kg/L |
|
Density of freshly mixed glue |
≈2.0kg/L |
|
Working time |
20-30min |
|
Time of upper finishing |
24-48hours |
|
Fluidity ratio (mm) Initial value |
≥130 |
|
20min |
≥130 |
|
Tensile adhesion strength Mpa |
≥1.0 |
|
Wear resistant test g |
≤0.5 |
|
Dimensional change rate % |
-0.15~+0.15 |
|
Impact resistant test |
No crack or peeling from base |
|
Rub fastness |
Passed (BS 8204:AR1) |
|
Construction |
Grouting |
|
Compressive strength force 24h |
10.3Mpa |
|
Compressive strength force 7d |
20Mpa (En196) |
|
Compressive strength force 28d |
27Mpa |
|
Bending strength force 24h |
3Mpa |
|
Bending strength force 7d |
6Mpa(En196) |
|
Bending strength force 28d |
7.7Mpa |
|
Falling ball rigidity 24h |
50Mpa |
|
Falling ball rigidity 7d |
55Mpa(Brine 11) |
|
Falling ball rigidity 28d |
80Mpa |
|
Lateral deformation ratio (load) N |
11 |
|
Lateral deformation ratio (deformatiton) mm |
1.6 |
|
Shelf life |
12 months |
|
Condition on site |
5-40℃ |